Effect of ultrasonic surface rolling on the surface integrity and wear resistance of IN718
编号：142
稿件编号：113 访问权限：仅限参会人
更新：2024-10-13 21:26:44
浏览：174次
张贴报告
报告开始：2024年10月19日 11:40 （Asia/Shanghai）
报告时间：20min
所在会议：[P0] Poster » [P0] Poster
暂无文件
摘要
Nickel-base superalloys have an irreplaceable position in the aerospace field due to their unique high temperature resistance and corrosion resistance. IN718 is susceptible to wear failure in harsh service environments, so high wear resistance is one of the desired properties of IN718 superalloy. In this paper, the optimal parameters of ultrasonic surface rolling process for IN718 were explored through orthogonal tests. Microstructure characterization, microhardness measurements, and wear resistance analysis at room temperature were carried out by laser confocal microscope, scanning electron microscope, X-ray diffractometer, microhardness tester and friction and wear testing machine. The results show that ultrasonic surface rolling can reduce the surface roughness of the material and increase the microhardness, which gradually decreased from the surface of the material to the core. In the friction and wear test with a load of 10N, it was found that the ultrasonic surface rolling process improved the anti-wear performance of IN718.
Nickel-base superalloys have an irreplaceable position in the aerospace field due to their unique high temperature resistance and corrosion resistance. IN718 is susceptible to wear failure in harsh service environments, so high wear resistance is one of the desired properties of IN718 superalloy. In this paper, the optimal parameters of ultrasonic surface rolling process for IN718 were explored through orthogonal tests. Microstructure characterization, microhardness measurements, and wear resistance analysis at room temperature were carried out by laser confocal microscope, scanning electron microscope, X-ray diffractometer, microhardness tester and friction and wear testing machine. The results show that ultrasonic surface rolling can reduce the surface roughness of the material and increase the microhardness, which gradually decreased from the surface of the material to the core. In the friction and wear test with a load of 10N, it was found that the ultrasonic surface rolling process improved the anti-wear performance of IN718.
Nickel-base superalloys have an irreplaceable position in the aerospace field due to their unique high temperature resistance and corrosion resistance. IN718 is susceptible to wear failure in harsh service environments, so high wear resistance is one of the desired properties of IN718 superalloy. In this paper, the optimal parameters of ultrasonic surface rolling process for IN718 were explored through orthogonal tests. Microstructure characterization, microhardness measurements, and wear resistance analysis at room temperature were carried out by laser confocal microscope, scanning electron microscope, X-ray diffractometer, microhardness tester and friction and wear testing machine. The results show that ultrasonic surface rolling can reduce the surface roughness of the material and increase the microhardness, which gradually decreased from the surface of the material to the core. In the friction and wear test with a load of 10N, it was found that the ultrasonic surface rolling process improved the anti-wear performance of IN718.
关键字
Ultrasonic surface rolling,Wear resistance,Surface integrity,IN718